The ANYCUBIC PLA-CF IPHPFFW-101 is a carbon-fiber reinforced PLA (PLA-CF) 3D printer filament supplied on a 1 kg spool. Reinforced with short carbon fibers for higher stiffness and improved mechanical properties suitable for functional prototypes and rigid parts. Color: White. Model/MPN:...
More
Anycubic PLA-CF Fish Scale 1kg 3D Printer Filament (IPHPFFW-101)
Product Code: 1167713179
Available in 4 - 6 days
26,56 €
With the purchase of this product you earn 80 Bytes
Quantity:
Add
Need Help? Fill in your details so we can call you immediately!
TBI Bank
Buy Now Pay Later.
4 installments 0% επιτόκιο, 20€ έως 300€
3 to 60 installments 300€ έως 100.00€
- 1. Ship with ACS Courier
- 2. Αποστολές με μεταφορικές εταιρίες για ογκώδη αντικείμενα
-
3. Pickup from BoxNow automated machine:
Με την BoxNow μπορείς να παραλάβεις το δέμα σου από Αυτόματο Μηχάνημα Παραλαβής που βρίσκεται κοντά σου, όλες τις ώρες της ημέρας 24/7. Η υπηρεσία έχει χρέωση 3€. Υπάρχει δυνατότητα αντικαταβολής με επιπλέον χρέωση 1€.
-
4. Pickup from the store:
Leof. El. Venizelou 73 (former Theseos), Kallithea
Συμπληρώστε τον ταχυδρομικό κωδικό για να λάβετε εκτίμηση τρόπου και κόστους μεταφορικών.
The ANYCUBIC PLA-CF IPHPFFW-101 is a carbon-fiber reinforced PLA (PLA-CF) 3D printer filament supplied on a 1 kg spool. Reinforced with short carbon fibers for higher stiffness and improved mechanical properties suitable for functional prototypes and rigid parts. Color: White. Model/MPN: IPHPFFW-101. EAN/SKU provided. Recommended nozzle size ≥ 0.4 mm (use hardened or wear-resistant nozzle due to abrasive fibers). Print temperature: 210–250 °C. Heated bed: 55–70 °C. Print speed range: 40–250 mm/s. Density: 1.22 g/cm³. Melting/printing reference temperature: ~165 °C. Tensile strength ~44 ± 3 MPa; flexural strength ~74 ± 5 MPa; flexural modulus ~3100 MPa. Filament form: spool. Manufacturer: Anycubic. Suitable for applications requiring increased stiffness and dimensional stability.
-
BrandAnycubic
-
Model / MPNIPHPFFW-101
-
Filament TypePLA-CF (PLA reinforced with carbon fiber)
-
Net Weight1 kg
-
ColorWhite
-
Filament FormSpool
-
Recommended Nozzle Diameter≥ 0.4 mm
-
Printing Temperature210–250 °C
-
Heated Bed Temperature55–70 °C
-
Printing Speed40–250 mm/s
-
Density1.22 g/cm³
-
Melting / Reference Temperature165 °C
-
Tensile Strength44 ± 3 MPa
-
Flexural Strength74 ± 5 MPa
-
Flexural Modulus / Stiffness≈ 3100 MPa
-
Special NotesContains carbon fiber — abrasive; use hardened/nozzle resistant to wear
-
Typical UsesFunctional prototypes, rigid parts, components requiring increased stiffness
Ratings
Description
The ANYCUBIC PLA-CF IPHPFFW-101 is a carbon-fiber reinforced PLA (PLA-CF) 3D printer filament supplied on a 1 kg spool. Reinforced with short carbon fibers for higher stiffness and improved mechanical properties suitable for functional prototypes and rigid parts. Color: White. Model/MPN: IPHPFFW-101. EAN/SKU provided. Recommended nozzle size ≥ 0.4 mm (use hardened or wear-resistant nozzle due to abrasive fibers). Print temperature: 210–250 °C. Heated bed: 55–70 °C. Print speed range: 40–250 mm/s. Density: 1.22 g/cm³. Melting/printing reference temperature: ~165 °C. Tensile strength ~44 ± 3 MPa; flexural strength ~74 ± 5 MPa; flexural modulus ~3100 MPa. Filament form: spool. Manufacturer: Anycubic. Suitable for applications requiring increased stiffness and dimensional stability.
Technical Specifications
-
BrandAnycubic
-
Model / MPNIPHPFFW-101
-
Filament TypePLA-CF (PLA reinforced with carbon fiber)
-
Net Weight1 kg
-
ColorWhite
-
Filament FormSpool
-
Recommended Nozzle Diameter≥ 0.4 mm
-
Printing Temperature210–250 °C
-
Heated Bed Temperature55–70 °C
-
Printing Speed40–250 mm/s
-
Density1.22 g/cm³
-
Melting / Reference Temperature165 °C
-
Tensile Strength44 ± 3 MPa
-
Flexural Strength74 ± 5 MPa
-
Flexural Modulus / Stiffness≈ 3100 MPa
-
Special NotesContains carbon fiber — abrasive; use hardened/nozzle resistant to wear
-
Typical UsesFunctional prototypes, rigid parts, components requiring increased stiffness